This research aimed to study the influence of stress concentration and temperature under tensile
testing on mechanical properties and microstructure of JIS G3135 SPFC440 high strength steels. Tensile
specimens, ASTM-E8 standard, were prepared into five different stress concentration patterns and the
four different tensile tests temperature were 25°C, 200°C, 400°C, and 600°C. The results showed that
the effect of stress concentration on the tensile strength of the material was significantly decreased. From
testing at room temperature as a ductile fracture is a result of the microstructure investigation of fracture
surface caused the dimples fracture comparing to the testing in high-temperature which loss ductility
from heat.
Keywords
High strength steel, Stress concentration, Mechanical properties, Microstructure